Polymer Core-Polymer Shell Particle Formation Enabled by Ultralow Interfacial Tension Via Internal Phase Separation: Morphology Prediction Using the Van Oss Formalism

Artikel i vetenskaplig tidskrift
Författare M. A. Trojer
Anna Ananievskaia
Asvad A Gabul-Zada
L. Nordstierna
Hans Blanck
Publicerad i Colloid and Interface Science Communications
Volym 25
Sidor 36-40
ISSN 2215-0382
Publiceringsår 2018
Publicerad vid Institutionen för biologi och miljövetenskap
Sidor 36-40
Språk en
Länkar dx.doi.org/10.1016/j.colcom.2018.07...
Ämnesord Microcapsule, Solvent evaporation, Core-shell, Raspberry, Janus, Spreading, microcapsules, release, encapsulation, Chemistry, Science & Technology - Other Topics, Materials Science
Ämneskategorier Nanoteknik, Kemi

Sammanfattning

The internal phase separation technique is a versatile method for liquid core-polymer shell formation, yet limited to very hydrophobic core materials and actives. The use of polymeric cores instead circumvents this restriction due to the absent mixing entropy for binary polymer mixtures which allows the polymeric core (and the active) to approach the polarity of the shell. Polystyrene core-shell and janus particles were formulated using polymethylmethacrylate, poly(lactic acid), poly(lactic acid-co-glycolic acid), poly(epsilon-caprolactone) or cellulose triacetate as shell-forming polymers. The morphology and the partitioning was experimentally determined by selectively staining the core and the shell with beta-carotene and methylene blue respectively. In addition, the van Oss formalism was introduced to theoretically predict the thermodynamic equilibrium morphology. As elucidated using the theoretical predictions as well as experimental optical tensiometry, it was found that the driving force for core-shell morphology is, in contrast to liquid core-polymer shell particles, a low core-shell interfacial tension.